3:1 Low Viscosity Bubble Free Fast Cure Clear Epoxy Resin
Model: 312AB-8 Mixing Ratio: 3:1 by weight
312AB-8 is a 3:1 low viscosity bubble-free epoxy resin for charms, badges, coated cards and miniature mold pieces. Its thin formula moves quickly across fine details and shallow surfaces, helping reduce trapped air during pouring and leveling. The resin suits small projects that need a clear, glossy finish without heavy post-correction. Fast curing shortens the wait between pouring and demolding, while the cured material keeps stable hardness for handling and display. This product fits silicone molds, keychain parts, badge coatings and mini decorative pieces where fluidity and bubble control matter.
Inquire
TDS
Low Viscosity. Clear as Water.
Formulated with low viscosity, this 3:1 epoxy resin offers exceptional bubble release and self-leveling capabilities. The cured result is nearly bubble-free with a smooth, wave-free surface. Clear as water, it empowers you to easily tackle small resin craft projects and bring out the finest details with perfection. For exquisite handmade creations — this is your go-to choice.
One Resin. Endless DIY Craft Possibilities.
Jinhua's 3:1 epoxy resin delivers low viscosity, fast curing, ultra clarity, and bubble-free performance. Whether you're making tiny jewelry, delicate ornaments, mini boxes, or small encapsulation projects, this resin handles it all with ease. One kit — endless creativity.
Packing
20KG per carton Standard packing is 5kgs per bottle, and 20kgs per set. Or you can choose any kind of bottle as below:
Specifications
| Item | Part A | Part B |
| Color | Transparent | Transparent |
| Mixing ratio | A:B=3:1(weight ratio) | |
| Viscosity(25℃) | 1500±3000cps | Max 100cps |
| Curing Time(25℃) | 8-10h | |
| Pot life | 40mins | |
| Gravity | 1.15 | 0.96 |
| Hardness(Shore D) | 85 | |
| Shelf Life | 1 year | 1 year |
FAQs
-
Does this model real bubble free?
-
Yes, this model is bubble free due to its low viscosity.
-
This model can be mixed by volume ratio?
-
This model is designed for weight ratio, if you want to mix by volume, make it about 2.7:1
-
Can i mix 3kgs A and 1kgs B per time?
-
We do not suggest to, this model designed for small casting or coating, not for big casting, if you use too much per time, it will release too much heat that will ruin your pieces.
-
What is the curing time for this model?
-
We test 2g mixture, ths curing time is 8-10hours at the temperature of 25degree, but if you mix more per time, the curing time will be shorter, we do suggest you to test it before your apply.